关键字：electrochemical impedance spectroscopy, high-nitrogennickel-free austenitic stainless steel, passive film,
摘要：A new smelting method to synthesize high-nitrogen nickel-free austenitic stainless steel was suggested. The synthesized steel completely consists of austenite and represents more brilliant anti-corrosion ability both in salt solution and sulfuric acid solution. The brilliant anti-corrosion ability is retained even after severe coldrolling deformation, which ensures its workability in practice. The potentiodynamic polarization curves,electrochemical impedance spectroscopy, and passivating treatment were used to characterize its corrosion properties and uncover its corrosion mechanism in salt solution. X-ray photoelectron spectroscopy was used to clarify the mechanism of passivation. The results demonstrate that the steel has a more uniform and thicker passive film than traditional stainless steel due to the cooperation of nitrogen and chromium.
合写作者：王国勇
第一作者：孙世成
论文类型：期刊论文
页面范围：1
是否译文：否
发表时间：2014-11-01