- 【SCI4区通讯作者宋晓锋】Synthesized polyurethane from p-toluenesulfonyl isocyanate and epichlorohydrin via salen catalysis
- 点击次数：
- 所属单位：化学工程学院
- 发表刊物：Materials Chemistry and Physics
- 项目来源：其他课题
- 摘要：Macromolecules with fluoroalkyl group are promising as anti-fouling materials. In the work, a series of polycaprolactone grafted poly(octafluoropentyl methacrylate-co-hydroxyethyl methacrylate)s (PCL-PFHs) were synthesized as additives to change the surface properties of poly(L-lactic acid) (PLLA). The synthesized products were characterized with 1HNMR and GPC. PCL-PFH and PLLA were immiscible in blend, but PCL-PFH microparticles could immerse uniformly in PLLA substrate. The molar ratio of [OFPA]/[HEMA] in PFH and blend ratio of PCL-PFH/PLLA played a key role in changing the surface properties of PLLA blend. When the molar ratio and blend ratio were 4/1 and 10/90 respectively, the surface tension of PLLA blend lowered to 19.57 mN m􀀀 1, and it inhibited BSA adhesion effectively during protein adsorption process. At the same time, PLLA blend presented good hydrolytic stability. PCL-PFH also toughened PLLA, and the tensile strength and elongation at a break were 37.0 MPa and 126.1%. Then this work would built a new bridge between PLLA materials and biomedical engineering.
- 合写作者：韩立彬
- 第一作者：宋晓峰
- 论文类型：期刊论文
- 卷号：278
- 页面范围：1
- 是否译文：否
- 发表时间：2022-01-01