关键字：Carbon fibers Bio-inspired Interface Surface modification

摘要：The weak interfacial adhesion between carbon fiber (CF) and resin matrix are the main factors limiting the performance of CF reinforced polymer composites. Therefore, it was necessary to modify the surface of CF, but most processes also confronted the problems of unsustainable and environmental pollution. Here, the ecofriendly bio-based gallic acid (GA) and gelatin (GE) were biomimetic co-deposited on the CF surface in aqueous solution. The co-depositing GA-GE coating adhered well to the surface of inert CF and significantly increased CF surface active functional groups and wettability, resulted in the interfacial shear strength increased by 78.7%, compared to the pristine CF/epoxy composites. Hence, it is a promising approach to significantly enhance the interfacial adhesion of CF/epoxy composites and expected to be used in industrial production.

合写作者：张孟杰,敖玉辉,敖玉辉

第一作者：金琳

论文类型：期刊论文

卷号：26

页面范围：1

是否译文：否

发表时间：2020-09-22